Typical Technical Parameters |
|
MAGNESITE BRICKS |
|
|
Product Brand |
SiO2%Max. |
MgO % Min. |
Cr2O3%Min. |
Fe2O3% Max. |
A.P.% Max. |
C.C.S. kgs/ cm2 Min. |
R.U.L. ta O,/supC (2Kg/ cm2)Min. |
Application |
RH-MAG |
6.5 |
86 |
- |
- |
22 |
350 |
1550 |
EAF, BOF, CHF, Ferrous & Non-Ferrous, cement & other general purpose |
RH- MAG |
5.5 |
8.7 |
- |
- |
22 |
350 |
1580 |
RH- MAGD |
6.5 |
87 |
- |
- |
22 |
500 |
1580 |
Low Porosity bricks for Copper Furnace & EAF Furnace |
RH- MAG-91 |
5.0 |
91 |
- |
1.0 |
18 |
500 |
1600 |
EAF, BOF, secondary steel making, non-ferrous, Low iron content for Glass& chemical industries. |
RH- MAG-95 |
1.5 |
95 |
- |
0.8 |
18 |
500 |
1700 |
RH- MAG-98 |
0.5 |
97.5 |
- |
0.25 |
17 |
600 |
1720± |
RH- MAG S/C |
- |
86 |
|
- |
14 |
400 |
1550 |
Chemically bonded with clad & without clad |
|
|
|